AgGaS2 siv lead ua


  • Lattice Parameters:a = 5.757, c = 10.311 Å
  • Melting Point:997°C kub
  • Ceev:4.702 g / cm3
  • Mohs Hardness:3-3.5
  • Absorption Coefficient:0.6cm-1 @ 10.6 µm
  • Tus txheeb ze Dielectric Constant @ 25:11s=10 11t=14
  • Product Detail

    Technical Parameters

    Test Report

    Daim ntawv teev npe

    AGS yog pob tshab los ntawm 0.50 mus rau 13.2 µm.Txawm hais tias nws cov nonlinear optical coefficient yog qhov qis tshaj ntawm cov hais txog infrared crystals, siab luv wavelength transparency edging ntawm 550 nm yog siv los ntawm OPOs pumped los ntawm Nd: YAG laser;nyob rau hauv ntau qhov sib txawv zaus sib xyaw ua ke nrog diode, Ti: Sapphire, Nd: YAG thiab IR dye lasers npog 3-12 µm ntau yam;nyob rau hauv ncaj qha infrared countermeasure systems, thiab rau SHG ntawm CO2 laser.Nyias AgGaS2 (AGS) siv lead ua daim hlau yog nrov rau ultrashort mem tes tiam nyob rau hauv nruab nrab IR ntau yam los ntawm qhov sib txawv zaus tiam siv NIR wavelength pulses.

    Daim ntawv thov:
    • Tiam thib ob harmonics ntawm CO thiab CO2 - lasers
    • Optical parametric oscilator
    • Lub tshuab hluav taws xob sib txawv mus rau thaj chaw nruab nrab infrared mus txog 12μm.
    • Kev sib xyaw zaus hauv nruab nrab IR cheeb tsam ntawm 4.0 txog 18.3 µm
    • Tuneable solid state lasers (OPO pumped los ntawm Nd:YAG thiab lwm yam lasers ua hauj lwm nyob rau hauv 1200 mus 10000 nm cheeb tsam nrog efficiency 0.1 mus rau 10 %)
    • Optical nqaim-band lim nyob rau hauv cheeb tsam ze isotropic point (0.4974 m ntawm 300 °K), kis band raug kho ntawm qhov kub thiab txias
    • Up-hloov ntawm CO2 laser hluav taws xob duab rau hauv ze-IR lossis pom thaj tsam los ntawm kev siv / lossis siv Nd:YAG, ruby ​​lossis dye lasers nrog efficiency txog li 30%
    Cov cuab yeej yooj yim
    Lattice parameters a = 5.757, c = 10.311 Å
    Tsis-linear coefficient ntawm 10.6 um d36 = 12.5 pm/V
    Optical puas pib ntawm 10.6 um, 150 ns 10-20 MW/cm2
    parallel rau c-axis 12.5 x 10-6 x °C-1
    perpendicular rau c-axis -13.2 x 10-6 x °C-1
    Crystal Structure Tetragonal
    Cell Parameters a = 5.756 Å, c = 10.301 Å
    Melting Point 997°C kub
    Qhov ntom 4.702 g / cm3
    Mohs Hardness 3-3.5
    Absorption Coefficient 0.6cm-1 @ 10.6 µm
    Tus txheeb ze Dielectric Constant @ 25 MHz 11s=10 11t=14
    Thermal Expansion Coefficient ||C: -13.2 x 10-6 /oC⊥C: +12.5 x 10-6 /oC
    Thermal conductivity 1.5 W / M / ° C

     

    Technical Parameters
    Wavefront distortion tsawg dua λ/6 @ 633 nm
    Dimension kam rau ua (W +/- 0.1 mm) x (H +/- 0.1 mm) x (L + 0.2 mm/- 0.1 mm)
    Clear aperture > 90% Central cheeb tsam
    Flatness λ/6 @ 633 nm rau T> = 1.0mm
    Nto Zoo Scratch/dig 20/10 per MIL-O-13830A
    Parallelism zoo tshaj 1 arc min
    Perpendicularity 5 arc nqi
    Lub kaum sab xis Δθ < +/- 0.25o, Δφ < +/- 0.25o

    测试图1图片2

    Qauv

    Khoom Loj Kev taw qhia Nto Mount

    Ntau

    TIAB SA 0053

    AGS 5 * 5 * 0.5 hli θ = 41.3 °; φ = 0 ° AR/AR@1.1-2.6μm+2.6-12μm Unmounted

    1

    TIAB SA 0093

    AGS 8 * 8 * 1mm θ = 39 °; φ = 45 ° Ob sab polished φ25.4 hli

    3

    DE0119-0

    AGS 8 * 8 * 1mm θ = 39 °; φ = 45 ° AR/AR@1.1-2.6μm+2.6-12μm φ25.4 hli

    3

    DE0119-3

    AGS 8 * 8 * 1mm θ = 39 °; φ = 45 ° AR/AR@1.1-2.6μm+2.6-12μm Unmounted

    2

    DE0119-1

    AGS 8 * 8 * 1mm θ = 37 °; φ = 45 ° AR/AR@1.1-2.6μm+2.6-12μm Unmounted

    3

    TIAB SA 0149

    AGS 8 * 8 * 0.38 hli θ = 41.6 °; φ = 45 ° AR/AR@1.1-2.6μm+2.6-12μm Unmounted

    1

    TIAB SA 0367

    AGS 8 * 8 * 0.4 hli θ = 39 °; φ = 45 ° AR/AR@1.1-2.6μm+2.6-12μm φ25.4 hli

    1

    TIAB SA 0367-0

    AGS 8 * 8 * 0.4 hli θ = 39 °; φ = 45 ° AR/AR@1.1-2.6μm+2.6-12μm Unmounted

    1

    TIAB SA 0367-1

    AGS 8 * 8 * 0.4 hli θ = 37 °; φ = 45 ° AR/AR@1.1-2.6μm+2.6-12μm Unmounted

    3

    TIAB SA 0367-2

    AGS 8 * 8 * 0.4 hli θ = 37 °; φ = 45 ° AR/AR@1.1-2.6μm+2.6-12μm φ25.4 hli

    1